Navegando por Assunto "Bioactive glass"

Agora exibindo 1 - 2 de 2
  • Imagem de Miniatura
    Item
    Biocomposite macrospheres based on strontium-bioactive glass for application as bone fillers
    (American Chemical Society) Oliveira, Ivone Regina de; Gonçalves, Isabela dos Santos; Santos, Kennedy Wallace dos; Lança, Maria Carmo; Vieira, Tânia; Silva, Jorge Carvalho; Cengiz, Ibrahim Fatih; Reis, Rui Luís; Oliveira, Joaquim Miguel; Borges, João Paulo Miranda Ribeiro
    Traditional bioactive glass powders are typically composed of irregular particles that can be packed into dense configurations presenting low interconnectivity, which can limit bone ingrowth. The use of novel biocomposite sphere formulations comprising bioactive factors as bone fillers are most advantageous, as it simultaneously allows for packing the particles in a 3-dimensional manner to achieve an adequate interconnected porosity, enhanced biological performance, and ultimately a superior new bone formation. In this work, we develop and characterize novel biocomposite macrospheres of Sr-bioactive glass using sodium alginate, polylactic acid (PLA), and chitosan (CH) as encapsulating materials for finding applications as bone fillers. The biocomposite macrospheres that were obtained using PLA have a larger size distribution and higher porosity and an interconnectivity of 99.7%. Loose apatite particles were observed on the surface of macrospheres prepared with alginate and CH by means of soaking into a simulated body fluid (SBF) for 7 days. A dense apatite layer was formed on the biocomposite macrospheres’ surface produced with PLA, which served to protect PLA from degradation. In vitro investigations demonstrated that biocomposite macrospheres had minimal cytotoxic effects on a human osteosarcoma cell line (SaOS-2 cells). However, the accelerated degradation of PLA due to the degradation of bioactive glass may account for the observed decrease in SaOS-2 cells viability. Among the biocomposite macrospheres, those composed of PLA exhibited the most promising characteristics for their potential use as fillers in bone tissue repair applications.
  • Imagem de Miniatura
    Item
    Calcium Aluminate Cement Blends Containing Bioactive Glass and Strontium for Biomaterial Applications
    (SciELO) Barbosa, Ana Margarida; Santos, Kennedy Wallace dos; Gonçalves, Irene S.; Leite, Priscila Maria Sarmeiro Corrêa Marciano; Martorano, Antonio Secco; Grisote, Gabriela; Raucci, Larissa Moreira Spinola de Castro; Oliveira, Paulo Tambasco de; Raniero, Leandro José; Oliveira, Ivone Regina de
    In this work blends based on calcium aluminate cement (CAC) containing bioactive glass (BG) (5, 7.5 and 10 wt%) and strontium oxide (1 wt%) were produced aiming improve their bioactivity and the capacity to stimulate the bone regeneration. In the first part, the blends containing only BG were characterized as theoretical density, microhardness, uniaxial cold crush strength after SBF and apparent porosity and pore size distribution before and after SBF treatment. In the second part, bioactivity and cell culture tests were also conducted in the blends containing BG and strontium oxide. The addition of 7.5 wt% of BG in homogeneous calcium aluminate cement (CH) improved its mechanical properties as microhardness and uniaxial cold crushing strength. The blends were more bioactive due to the presence of a highly soluble amorphous phase as confirmed by means of SEM/EDX mainly for 7.5 wt% BG without and with Sr from 1 day in SBF. FTIR analyses indicated the formation the apatite-like phase by means of increase of intensity of the PO43- peaks after SBF treatment. All blends allowed the development of the osteoblastic phenotype and the formation of mineralized matrix increased due to the inclusion of BG and Sr promoting the osteogenesis process.